参数资料
| 型号： | 2-5-4949 |
| 厂商： | 3M (TC) |
| 文件页数： | 9/11页 |
| 文件大小： | 0K |
| 描述： | TAPE VHB BLACK 2" GEN PURPOSE |
| 视频文件： | 3M VHB adhesive demonstration - Another Geek Moment |
| MSDS 材料安全数据表： | 49zz MSDS |
| 标准包装： | 1 |
| 系列： | VHB™ 4949 |
| 胶带类型： | 双涂层，双面 |
| 胶合剂： | 丙烯酸 |
| 背衬，载体： | 聚酯薄膜 |
| 厚度： | 0.045"（45 mils，1.143mm） |
| 厚度 - 胶合剂： | 0.043"（43 mils，1.092mm） |
| 厚度 - 背胶，载体，衬垫： | 0.0020"（2.0 mils，0.051mm） |
| 宽： | 2.00"（50.80mm） |
| 长度： | 15'（4.6m）5 码 |
| 颜色： | 黑 |
| 使用： | 通用 |
| 温度范围： | 200°F（93°C） |
| 包装： | 散装 |
| 其它名称： | 3M10138 |
3M ? VHB ? Tapes
Application Techniques
Clean: Most substrates are best prepared by cleaning with a 50:50 mixture of isopropyl alcohol (IPA*) and
water prior to applying 3M? VHB? Tapes.
Exceptions to the general procedure that may require additional surface preparation include:
? Heavy Oils: A degreaser or solvent-based cleaner may be required to remove heavy oil or grease from a
surface and should be followed by cleaning with IPA/water.
? Abrasion: Abrading a surface, followed by cleaning with IPA/water, can remove heavy dirt or oxidation
and can increase surface area to improve adhesion.
? Adhesion Promoters: Priming a surface can significantly improve initial and ultimate adhesion to many
materials such as plastics and paints.
? Porous surfaces: Most porous and fibered materials such as wood, particleboard, concrete, etc. need to be
sealed to provide a unified surface.
? Unique Materials: Special surface preparation may be needed for glass and glass-like materials, copper
and copper containing metals, and plastics or rubber that contain components that migrate (e.g. plasticizers).
Refer to 3M Technical Bulletin “Surface Preparation for 3M? VHB? Tape Applications” for additional
details and suggestions. (70-0704-8701-5)
*Note: These cleaner solutions contain greater than 250 g/l of volatile organic compounds (VOC). Please
consult your local Air Quality Regulations to be sure the cleaner is compliant. When using solvents,
be sure to follow the manufacturer ’s precautions and directions for use when handling such materials.
Pressure: Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm
application pressure develops better adhesive contact and helps improve bond strength. Typically, good surface
contact can be attained by applying enough pressure to insure that the tape experiences approximately 15 psi
(100 kPa) pressure. Either roller or platen pressure can be used. Note that rigid surfaces may require 2 or 3 times
that much pressure to make the tape experience 15 psi.
Temperature: Ideal application temperature range is 70°F to 100°F (21°C to 38°C). Pressure sensitive
adhesives use viscous flow to achieve substrate contact area. Minimum suggested application temperatures:
? 50°F (10°C): 3M? VHB? Tapes 4950, 5952, 4910, 4952, 4611, 4622 families.
? 60°F (15°C): 3M? VHB? Tapes 4941, 4945 families.
? 32°F (0°C): 3M? VHB? Tape 4951 families.
Note: Initial tape application to surfaces at temperatures below these suggested minimums is not
recommended because the adhesive becomes too firm to adhere readily. However, once properly
applied, low temperature holding is generally satisfactory.
To obtain good performance with all 3M? VHB? Tapes, it is important to ensure that the surfaces are dry
and free of condensed moisture.
Time: After application, the bond strength will increase as
Bond Typical Build vs. Time
●
★
★
●
●
the adhesive flows onto the surface (also referred to as “wet out”).
At room temperature approximately 50% of ultimate bond
strength will be achieved after 20 minutes, 90% after 24 hours
and 100% after 72 hours. This flow is faster at higher temperatures
and slower at lower temperatures. Ultimate bond strength can be
achieved more quickly (and in some cases bond strength can be
increased) by exposure of the bond to elevated temperatures
60
20
PERCENT OF FULL BOND
100 ■ ■ ■
■ ●
●
80 ■ ●
●
●
★
40 ★
★
■
●
★
■
●
★
■
●
■
★
■
★
■
★
●
■ ●
★
●
★
●
★
(e.g. 150°F [66°C] for 1 hour). This can provide better adhesive
wetout onto the substrates. Abrasion of the surfaces or the use of
0
20 MIN
1 HOUR 24 HOURS
● ROOM TEMP ★ 50°F
■ 150°F or ABRADE
72 HOURS
primers/ adhesion promoters can also have the effect of increasing
bond strength and achieving ultimate bond strength more quickly.
-9-
相关PDF资料 |
PDF描述 |
|---|---|
| 0395332012 | 5.08MM EURO PLUG STR BLK 12POS |
| 0395161017 | 3.81MM EURO HEADER RA BLK 17POS |
| 0395310017 | 5.08MM EURO HEADER STR BLK 17POS |
| 0395105215 | 3.81MM EURO PLUG RA GRN 15POS |
| 644460-7 | CONN RCPT 7POS 18AWG MTA-156 |
相关代理商/技术参数 |
参数描述 |
|---|---|
| 25-495 | 制造商:Distributed By MCM 功能描述:6.3V 35MA MICRO SIZE LAMP |
| 25495 BK005 | 功能描述:10 (5 Pair Twisted) Conductor Multi-Pair Cable Black 24 AWG Foil 100.0' (30.5m) 制造商:alpha wire 系列:Xtra-Guard? 2 零件状态:有效 电缆类型:多线对 导体数:10（5 对双绞线） 线规:24 AWG 导线股数:7/32 导体材料:铜，镀锡 护套（绝缘）材料:聚氨脂（PU） 护套（绝缘）直径:0.268"（6.80mm） 屏蔽类型:箔 长度:100.0'（30.5m） 套管颜色:黑 等级:ISO 10993，UL 式 20668 特性:生物相容性，加蔽线，拉绳 电压:300V 工作温度:-30°C ~ 90°C 使用:- 导体绝缘:聚氯乙烯（PVC） 护套（绝缘）厚度:0.032"（0.81mm） 屏蔽材料:铝 屏蔽范围:1 标准包装:10 |
| 2-5-4950 | 功能描述:TAPE VHB WHITE 2" GEN PURPOSE RoHS:是 类别:胶带，粘合剂 >> 带 系列:VHB™ 4950 MSDS 材料安全数据表:2393 MSDS 标准包装:40 系列:Scotch® 2393 胶带类型:屏蔽，高温 胶合剂:橡胶 背衬，载体:绉纸 厚度:0.0076"（7.6 mils，0.193mm） 厚度 - 胶合剂:- 厚度 - 背胶，载体，衬垫:- 宽:1.42"（36.00mm） 长度:180'（55.0m）60 码 颜色:棕褐 使用:喷漆，自动 温度范围:325°F（163°C）- 30 分钟 包装:- 其它名称:000212007130330212007130370006165651 |
| 2-5-4951 | 功能描述:TAPE VHB WHITE 2" LOW TEMP RoHS:是 类别:胶带，粘合剂 >> 带 系列:VHB™ 4951 MSDS 材料安全数据表:2393 MSDS 标准包装:40 系列:Scotch® 2393 胶带类型:屏蔽，高温 胶合剂:橡胶 背衬，载体:绉纸 厚度:0.0076"（7.6 mils，0.193mm） 厚度 - 胶合剂:- 厚度 - 背胶，载体，衬垫:- 宽:1.42"（36.00mm） 长度:180'（55.0m）60 码 颜色:棕褐 使用:喷漆，自动 温度范围:325°F（163°C）- 30 分钟 包装:- 其它名称:000212007130330212007130370006165651 |
| 2-5-4952 | 功能描述:TAPE VHB CLEAR 2" LOW SURFACE RoHS:是 类别:胶带，粘合剂 >> 带 系列:VHB™ 4952 MSDS 材料安全数据表:2393 MSDS 标准包装:40 系列:Scotch® 2393 胶带类型:屏蔽，高温 胶合剂:橡胶 背衬，载体:绉纸 厚度:0.0076"（7.6 mils，0.193mm） 厚度 - 胶合剂:- 厚度 - 背胶，载体，衬垫:- 宽:1.42"（36.00mm） 长度:180'（55.0m）60 码 颜色:棕褐 使用:喷漆，自动 温度范围:325°F（163°C）- 30 分钟 包装:- 其它名称:000212007130330212007130370006165651 |
发布紧急采购，3分钟左右您将得到回复。