参数资料
| 型号： | BSTS-04X4 |
| 厂商： | TE Connectivity |
| 文件页数： | 4/4页 |
| 文件大小： | 0K |
| 描述： | HEAT SHRINK TUBING |
| 标准包装： | 20 |
| 系列： | BSTS |
| 类型： | 套管，弹性 |
| 收缩比率： | 3 至 1 |
| 内径 - 提供： | 0.400"（10.2mm） |
| 内径 - 恢复： | 0.150"（3.8mm） |
| 已恢复的墙壁厚度： | 0.060"（1.52mm） |
| 材质： | 聚烯烃 |
| 特点： | 防水 |
| 颜色： | 黑 |
| 其它名称： | CB5004-000 |
Page 4
SPECIFICATION RW-2017 ISSUE 7
TABLE 2
REQUIREMENTS
PROPERTY
UNIT
BSTS BSTS -FR
TEST METHOD
PHYSICAL
Dimensions
Longitudinal Change
mm
(inch)
percent
In accordance with
Table 1
+1, - 10
In accordance with
Table 1
+1, -10
Section 6.1
ASTM D 2671
Section 6.1
ASTM D 2671
Tensile Strength
MPa (psi)
8.4 (1,200) minimum
8.4 (1,200) minimum
Section 6.2
ASTM D 638
Ultimate Elongation
percent
300 minimum
200 minimum
Section 6.2
ASTM D 638
2% Secant Modulus (Expanded)
Specific Gravity
Low Temperature Flexibility
MPa (psi)
N/A
1.1 maximum
No cracking
172.4 (25,000) maximum
1.5 maximum
No cracking
ASTM D 882
ASTM D 792
SAE-AMS-DTL-23053
4 hours at -55 ± 2 ° C
Heat Shock
4 hours at 225 ± 3 ° C
No dripping, flowing
or cracking
No dripping, flowing
or cracking
SAE-AMS-DTL-23053
Heat Resistance
168 hrs at 175 ± 2 ° C
Followed by tests for:
Tensile Strength
Ultimate Elongation
ELECTRICAL
Dielectric Strength
Volume Resistivity
MPa (psi)
percent
kV/mm
(V/mil)
ohm-cm
7.0 (1,000) minimum
100 minimum
7.9 (200) minimum
10 13 minimum
7.0 (1,000) minimum
100 minimum
7.9 (200) minimum
10 13 minimum
ASTM D 638
ASTM D 638
ASTM D 2671
*Note 1
ASTM D 876
CHEMICAL
Copper Mirror Corrosion
No removal of copper
No removal of copper
SAE-AMS-DTL-23053
16 hours at 120 ± 2 o C
Copper Contact Corrosion
16 hours at 120 ± 2 ° C
No pitting or
blackening of copper
No pitting or
blackening of copper
SAE-AMS-DTL-23053
Flammability
seconds
N/A
60 maximum
SAE-AMS-DTL-23053
(ASTM D 2671
Procedure C)
Water Absorption
percent
0.5 maximum
0.5 maximum
ASTM D 570
24 hours at 23 ± 2 ° C
Fungus Resistance
Followed by tests for:
ISO 846 Method B
Tensile Strength
Ultimate Elongation
Dielectric Strength
MPa (psi)
percent
kV/mm
8.4 (1,200) minimum
300 minimum
7.9 (200) minimum
8.4 (1,200) minimum
200 minimum
7.9 (200) minimum
ASTM D 638
ASTM D 638
ASTM D 2671
(V/mil)
Fluid Resistance
24 hours at 23 ± 2 ° C
JP-8 Fuel (MIL-DTL-83133)
Hydraulic Fluid (MIL-H-5606)
De-icing Fluid ( SAE-AMS-
1424 )
Lube Oil (MIL-PRF-7808)
Lube Oil (MIL-L-23699)
SAE-AMS-DTL-23053
5% NaCl (A-A-694)
Followed by tests for:
Tensile Strength
Ultimate Elongation
Dielectric Strength
MPa (psi)
percent
kV/mm
(V/mil)
5.2 (750) minimum
100 minimum
7.9 (200) minimum
5.2 (750) minimum
100 minimum
7.9 (200) minimum
ASTM D 638
ASTM D 638
ASTM D 2671
*Note 2
*Note 1: Recover specimens on the metal mandrels for 10 minutes minimum at 200 ± 3 ° C or until the tubing is completely
recovered on the mandrels.
*Note 2: For dielectric strength, immerse the recovered specimens in the fluids for 24 hours at 50 ± 2°C. After drying, place the
specimens over closest fitting metal mandrels.
If this document is printed it becomes uncontrolled. Check the latest revision.
相关PDF资料 |
PDF描述 |
|---|---|
| PLX1E820MCL1TD | CAP ALUM 82UF 25V 20% RADIAL |
| CB5291-000 | HEAT SHRINK TUBING |
| 608953-1 | HEAT SHRINK TUBING 1.50"X12" |
| H6PPS-1636M | DIP CABLE - HDP16S/AE16M/HDP16S |
| CB5310-000 | HEAT SHRINK TUBING |
相关代理商/技术参数 |
参数描述 |
|---|---|
| BSTS-04X4 | 制造商:TE Connectivity 功能描述:HEAT SHRINK 10.2MM BLACK 1.2M |
| BSTS-04X4/NM | 制造商:TE Connectivity 功能描述:CL3006-000 |
| BSTS-04X4-CL | 制造商:TE Connectivity 功能描述: |
| BSTS-04X4FR | 制造商:TE Connectivity 功能描述:CB5005-000 |
| BSTS-04X4-RSU | 制造商:TE Connectivity 功能描述:Thick wall heatshrink tubing,10.2mm i/d |
发布紧急采购，3分钟左右您将得到回复。