参数资料
| 型号： | 62-2324-2001-8 |
| 厂商： | 3M |
| 文件页数： | 5/8页 |
| 文件大小： | 0K |
| 描述： | TAPE SCOTCH-WELD 4IN X 36YD |
| MSDS 材料安全数据表： | 62-2324-2001-8 MSDS |
| 标准包装： | 10 |
| 系列： | Scotch-Weld™ |
| 胶带类型： | 薄膜 |
| 胶合剂： | 环氧树脂，热固性 |
| 背衬，载体： | 绉纸 |
| 厚度： | 0.0179"?（17.9 密耳，0.455mm） |
| 厚度 - 胶合剂： | 0.0100"（10.0 mils，0.254mm） |
| 厚度 - 背胶，载体，衬垫： | 0.0079"?（7.9 密耳，0.201mm） |
| 宽： | 4.00"（101.60mm）1/3' |
| 长度： | 108'（32.9m）36 码 |
| 颜色： | 灰白 |
| 使用： | 胶合 |
| 温度范围： | 250°F（121°C）- 60 分钟 |
| 包装： | 散装 |
| 其它名称： | Q5481988 |
3
Bonding Film
AF111 for Electronics Applications
Adhesion Retention
Values After
Environmental Aging
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Aging Parameters
30 days at room temperature (control)
30 days at 160°F (71°C) oven
30 days at 120°F (49°C)/100% RH
30 days immersion in distilled water
Hot/cold cycling
3M? Bonding Film AF111 Peel*
33 piw
33 piw
32 piw
35 piw
33 piw
* Peel bonds consisted of 10 mil etched aluminum strips bonded to 0.047" FR-4. Panels were
cured 60 minutes + 7 minutes (ramp time) at 250°F (121°C) and peeled at 2"/minute speed.
? Hot/cold cycle was 17 hours at 120°F (49°C) and 5 hours at -5°F (-21°C) with one hour at
room temperature between temperature changes.
Aging Parameters
30 days at room temperature (control)
30 days at 160°F (71°C) oven
30 days at 120°F (49°C)/100% RH
30 days immersion in distilled water
Hot/cold cycling
Bonding Film AF111 OLS*
2300 psi
2600 psi
1200 psii
1600 psi
2400 psi
* OLS (overlap shear) bonds consisted of 3M? Scotch-Brite? Scour Pad (green) abraded
CRS to CRS, cured 60 minutes + 7 minutes (ramp time) at 250°F (121°C) and tested at
0.2"/minute speed.
? Hot/cold cycle was 17 hours at 120°F (49°C) and 5 hours at -5°F (-21°C) with one hour at
room temperature between temperature changes.
Solvent Resistance of
Cured Films After 60
Days Immersion at RT
Aging Parameters
Isopropyl Alcohol
Methyl Ethyl Ketone
Heptane
3M? Citrus Base Cleaner
Bonding Film AF111
No Attack
No Attack
No Attack
No Attack
? Samples were cured according to data sheet instructions [60 minutes at 250°F (121°C)]
and immersed in test solvents.
? After 60 days, samples were removed, dried, and examined for swelling and surface attack.
-5-
相关PDF资料 |
PDF描述 |
|---|---|
| 62-9171-9153-8 | MIXING NOZZLE 50ML SHORT 3.25" |
| 62-9742-9935-6 | MIXING NOZZLE 50ML LONG 6.25" |
| 62-GRAY-1"X36YD | TAPE PTFE FILM BONDABLE 1"X 36YD |
| 621-037-268-032 | CONN D SUB PLUG 37POS R/A .318 |
| 624-025-661-032 | CONN D SUB RCPT 25POS R/A .200 |
相关代理商/技术参数 |
参数描述 |
|---|---|
| 6-2232532-3 | 功能描述:3P, PL RAST 5 TAB HEADER, TH,VER 制造商:te connectivity amp connectors 系列:* 零件状态:有效 标准包装:6,000 |
| 6-2232580-3 | 功能描述:3P, PL RAST 5 TAB HEADER, TH,VER 制造商:te connectivity amp connectors 系列:- 包装:散装 零件状态:在售 连接器类型:接头 触头类型:接片 间距 - 配接:0.197"（5.00mm） 针脚数:3 排数:1 行间距 - 配接:- 加载的针脚数:全部 样式:板至电缆/导线 护罩:带遮蔽 - 4 墙 安装类型:通孔 端接:焊接 紧固类型:锁存器支座 接触长度?- 配接:- 接触长度 - 接线柱:0.138"（3.50mm） 总体接触长度:- 绝缘高度:0.504"（12.80mm） 触头形状:矩形 触头表面处理 - 配接:锡 触头表面处理厚度 - 配接:- 触头表面处理 - 柱:锡 触头材料:黄铜 绝缘材料:聚酰胺（PA），尼龙 特性:板件导轨，兼容灼热丝规范 工作温度:-40°C ~ 120°C 侵入防护:- 材料可燃性等级:UL94 V-0 绝缘颜色:黑色 额定电流:- 额定电压:250VAC 接合堆叠高度:- 触头表面处理厚度 - 柱:- 应用:通用 标准包装:4,000 |
| 622326-000 | 制造商:TE Connectivity 功能描述:55PC0214-24-9CS2970 - Cable Rools/Shrink Tubing |
| 622330-000 | 制造商:TE Connectivity 功能描述:RHSTTN200-2-0-SP |
| 6223-32.768M | 制造商:CONNOR-WINFIELD 制造商全称:Connor-Winfield Corporation 功能描述:3.3V LVCMOS Surface Mount Crystal Clock Oscillator |
发布紧急采购，3分钟左右您将得到回复。